Negative magnetization and zero-field cooled exchange bias effect in Eu0.9Pr0.1CrO3 ceramics

作者：Huang, Ping; Deng, Dongmei^*; Zheng, Jiashun; Li, Qing; Feng, Zhenjie; Kang, Baojuan; Ren, Wei; Jing, Chao; Zhang, Jincang; Cao, Shixun

来源：Physica B: Condensed Matter , 2018, 530: 95-100.

DOI：10.1016/j.physb.2017.10.108

• Perovskite
• Canted antiferromagnetism
• Zero-field cooled exchange bias
• Negative magnetization
• Magnetic inhomogeneity

Interesting magnetic behaviors, including negative magnetization, zero field fooled and field cooled exchange bias effects, have been observed in Eu0.9Pr0.1CrO3. The negative magnetization at low temperature results from the antiparallel coupling between the Pr3+ moment and the canted moment of Cr3+ sublattice. Left shift of zero field cooled M-H loops, and right shift of field cooled M-H loops have been observed, due to the growth and competition of two types of magnetic structures with G(x)F(z) (EuCrO3) and G(z)F(x) (PrCrO3) orderings under magnetic field. When the cooling field is high enough, the Pr3+ moment is frozen antiparallel with the applied field during the cooling process, giving rise to a positive exchange bias (right shift of M-H). However, when the cooling field is near zero, magnetic clusters with G(x)F(z) (EuCrO3) or G(z)F(x) (PrCrO3) orderings are formed and distribute randomly during the cooling process, and the net Pr3+ moment get aligned along the applied field during the initial magnetization process to lower the Zeeman energy, and then negative exchange bias (left shift of M-H) appears.

• 出版日期2018-2-1
• 单位上海大学