Dense plasma focus ion-based titanium nitride coating on titanium

作者：Hassan M^*; Qayyum A; Ahmad R; Rawat R S; Lee P; Hassan S M; Murtaza G; Zakaullah M

来源：Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms , 2009, 267(11): 1911-1917.

DOI：10.1016/j.nimb.2009.03.102

• TiN
• Scanning electron microscopy (SEM)
• EDS
• X-ray diffraction
• Microstructure
• Surface properties

We report the synthesis of titanium nitride coating on a titanium substrate by utilizing energetic nitrogen ions emitted from a 2.3 kJ dense plasma focus device for 30 focus shots. The number of nitrogen ions transferred to the sample by a single ion pulse of about 140 ns duration in the energy interval (40-600 keV) is about 1.09 x 10(12) with a mean energy per ion of 58 keV. The corresponding energy flux delivered to the titanium surface is estimated to be 6.17 x 10(14) keV cm(-3) ns(-1) leading to a transient temperature rise of the top layer of about 5400 K which helps layer growth. The coating is investigated on the basis of its morphological, compositional and hardness properties. X-ray diffraction analysis of the sample reveals the formation of a nanocrystalline titanium nitride coating having (1 1 1) and (2 0 0) plane reflections with an average crystallite size of 40 nm. The compressive residual stresses in the nitride coating have been evaluated to be 2.80 GPa and 6.81 GPa corresponding to (1 1 1) and (2 0 0) plane orientations. A complete restructuring of the manually polished titanium substrate has been observed with appearance of nanosized multidimensional granular surface morphologies. The thickness of the nitride coating is about 1 mu m, whereas the coating has a nitrogen content of 35.35 at.% and 13.78 +/- 3.57 wt.% and a surface hardness of 8.19 GPa.

• 出版日期2009-6-1
• 单位南阳理工学院