Decoration of hierarchical Au/Pd nanostructures on 3C-SiC nanorods

作者：Khan Afzal; Jacob Chacko^*

来源：Materials Letters, 2015, 148: 50-54.

DOI：10.1016/j.matlet.2015.02.057

• 3C-SiC nanorods
• Chemical vapor deposition
• Hierarchical nanostructures
• Au/Pd coating
• Physical adsorption
• Sputtering

Fabrication of hierarchical nanostructures offers many advantages and can be exploited for creating superhydrophobic surfaces as well as heterojunctions and branched nanostructures, etc. In this work, catalytic growth of cubic-silicon carbide (3C-SiC) nanorods was carried out in an inductively heated horizontal cold-wall atmospheric pressure chemical vapor deposition (APCVD) reactor operated at the growth temperature i.e., 1200 degrees C for 1 h. Following this, hierarchical nanostructures of Au/Pd metal alloy were deposited on the surface of micron size long nanorods by DC sputtering. These hierarchical nanostructures were physically adsorbed on the surface of nanorods covering the exposed area. The average diameter of the nanorods as well as the average size of the adsorbed Au/Pd nanostructures was found to be in the range of 10-80 nm and 2-10 nm, respectively.

• 出版日期2015-6-1