Microstructure and superconducting properties of YBa2Cu3O7-delta thin films incorporated with a self-assembled magnetic vertically aligned nanocomposite

作者：Tsai Chen Fong^*; Lee Joon Hwan; Wang Haiyan

来源：Superconductor Science and Technology, 2012, 25(7): 075016.

DOI：10.1088/0953-2048/25/7/075016

A thin layer of a vertically aligned nanocomposite (VAN) with separated phases of ferromagnetic Fe2O3 and non-magnetic CeO2, arranged as alternating nanopillars, is introduced in YBa2Cu3O7-delta (YBCO) thin films as either a cap or a buffer layer using a pulsed laser deposition method. Detailed microstructural characterization including XRD, high resolution XTEM and STEM is conducted and correlated with the superconducting properties to investigate the flux pinning properties introduced by the magnetic VAN layers. The T-c values of both doped samples are above 89 K and the J(c)(sf) measured at 65 K increased to 150% of that of the reference YBCO prepared under the same conditions. As the measurement temperature decreases, the magnetic pinning effect increases and the field dependent J(c)(H parallel to c) is further improved to more than 200% of the J(c) value of the reference YBCO sample. This suggests that the Fe2O3:CeO2 VAN can provide both ordered magnetic pillars and controlled defect density. Furthermore, the magnetic pillars are very effective pinning centers especially in the high field and low temperature regime.

• 出版日期2012-7