Damage morphology study of high cycle fatigued as-cast Mg-3.0Nd-0.2Zn-Zr (wt.%) alloy

作者：Yue, Haiyan; Fu, Penghuai^*; Peng, Liming; Li, Zhenming; Pan, Jipeng; Ding, Wenjiang

来源：Materials Characterization, 2016, 111: 93-105.

DOI：10.1016/j.matchar.2015.11.013

• Mg alloy
• Fatigue damage mechanism
• Persistent slip marking
• Twinning band
• Grain orientation

Laser scanning confocal microscopy (LSCM) and Electron back-scattered diffraction (EBSD) were applied to the study of surface morphology variation of as-cast Mg-3.0Nd-0.2Zn-Zr (NZ30K) (wt.%) alloy under tension-compression fatigue test at room temperature. Two kinds of typical damage morphologies were observed in fatigued NZ30K alloy: One was parallel lines on basal planes led by the cumulation of basal slips, called persistent slip markings (PSMs), and the other was lens shaped, thicker and in less density, led by the formation of twinning. The surface fatigue damage morphology evolution was analyzed in a statistical way. The influences of stress amplitude and grain orientation on fatigue deformation mechanisms were discussed and the non-uniform deformation among grains and the PSMs, within twinning were described quantitatively.

• 出版日期2016-1
• 单位上海交通大学