Titanium alloys own a series of advantages such as low density, high specific strength, and biocompatibility. However, the poor wear resistance of titanium alloys impedes their wide applications in industry. In this study, we show that the wear resistance of the Ti6Al4V alloy can be greatly improved by a combined method of magnetron sputtering and plasma electrolytic oxidation (PEO). An similar to 13 pm pure aluminum layer was first applied on the Ti6Al4V alloy by magnetron sputtering and then PEO was employed for the second step treatment of the Al coated Ti6Al4V alloy. The PEO of the Al coated Ti6Al4V was carried out in aluminate (32 g l(-1)) and silicate (16 gl(-1)) electrolytes, respectively. Ball-on-disc tribological tests with an applied load of 10 N against a Cr steel ball were used to evaluate the wear performances of the samples. The coating formed in 32 gl(-1) aluminate electrolyte for 4 min shows superior wear performance, which sustained 1800 s sliding time against the steel ball and the wear rate is non-detectable. In contrast, the coating formed in the silicate electrolyte for 15 min has been destroyed during the tribological test, showing a wear rate of similar to 3.9 x 10(-4) mm(3)/(N.m). The excellent wear performance of the coatings formed in the aluminate electrolyte can be attributed to its high growth rate and homogeneity in microstructure. The coating growth mechanisms have also been discussed.
- 出版日期2019-1-25
- 单位湖南大学