Tailoring the diameter of single-walled carbon nanotubes for optical applications

作者：Tian Ying; Timmermans Marina Y; Kivisto Samuli; Nasibulin Albert G^*; Zhu Zhen; Jiang Hua; Okhotnikov Oleg G; Kauppinen Esko I

来源：Nano Research, 2011, 4(8): 807-815.

DOI：10.1007/s12274-011-0137-6

• Single-walled carbon nanotube
• diameter-controlled synthesis
• optical absorption spectroscopy
• saturable absorption
• mode-locked laser

Single-walled carbon nanotubes (SWCNTs) with specific diameters are required for various applications particularly in electronics and photonics, since the diameter is an essential characteristic determining their electronic and optical properties. In this work, the selective growth of SWCNTs with a certain mean diameter is achieved by the addition of appropriate amounts of CO(2) mixed with the carbon source (CO) into the aerosol (floating catalyst) chemical vapor deposition reactor. The noticeable shift of the peaks in the absorption spectra reveals that the mean diameters of the as-deposited SWCNTs are efficiently altered from 1.2 to 1.9 nm with increasing CO(2) concentration. It is believed that CO(2) acts as an etching agent and can selectively etch small diameter tubes due to their highly curved carbon surfaces. Polymer-free as-deposited SWCNT films with the desired diameters are used as saturable absorbers after stamping onto a highly reflecting Ag-mirror using a simple dry-transfer technique. Sub-picosecond mode-locked fiber laser operations at similar to 1.56 mu m and similar to 2 mu m are demonstrated, showing improvements in the performance after the optimization of the SWCNT properties.

• 出版日期2011-8