Mechanically robust 3D graphene macroassembly with high surface area

作者：Worsley Marcus A^*; Kucheyev Sergei O; Mason Harris E; Merrill Matthew D; Mayer Brian P; Lewicki James; Valdez Carlos A; Suss Matthew E; Stadermann Michael; Pauzauskie Peter J; Satcher Joe H Jr; Biener Juergen; Baumann Theodore F

来源：Chemical communications, 2012, 48(67): 8428-8430.

DOI：10.1039/c2cc33979j

We report the synthesis of a three-dimensional (3D) macroassembly of graphene sheets with electrical conductivity (similar to 10(2) S m(-1)) and Young's modulus (similar to 50 MPa) orders of magnitude higher than those previously reported, super-compressive deformation behavior (similar to 60% failure strain), and surface areas (>1300 m(2) g(-1)) approaching theoretically maximum values.