A comparison between fracture toughness at different locations of longitudinal submerged arc welded and spiral submerged arc welded joints of API X80 pipeline steels

作者：Chen Xu; Lu Hongsheng; Chen Gang; Wang Xin^*

来源：Engineering Fracture Mechanics, 2015, 148: 110-121.

DOI：10.1016/j.engfracmech.2015.09.003

• Fracture toughness
• X80 pipeline steel
• Welded joints
• Single specimen technique
• Precipitate Single-edge-notched bending specimen

In this paper, extensively experimental testing of fracture toughness for two different welded joints of API X80 pipeline steels after service were carried out. The microstructures and CTOD resistance curves of longitudinal submerged arc welded (LSAW) and spiral submerged arc welded (SSAW) joints were investigated at different locations of the base metal (BM), weld metal (WM) and heat affected zone (HAZ). The critical fracture toughness values were compared with each other. The optical microscope (OM), scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) were used to analyze the fracture mechanism and precipitates composition. This investigation will provide an important reference to engineering practice and evaluation of pipeline structures.

• 出版日期2015-11
• 单位天津大学