Morphological, chemical and structural characterisation of deciduous enamel: SEM, EDS, XRD, FTIR and XPS analysis

作者：Zamudio Ortega C M^*; Contreras Bulnes R; Scougall Vilchis R J; Morales Luckie R A; Olea Mejia O F; Rodriguez Vilchis L E

来源：European Journal of Paediatric Dentistry, 2014, 15(3): 275-280.

• Deciduous enamel
• energy dispersive-X-ray Spectroscopy
• Infrared spectroscopy
• Scanning electron microscopy
• x-ray diffraction
• X-ray photoelectron spectroscopy

Aim The purpose of this study was to characterise the enamel surface of sound deciduous teeth in terms of morphology, chemical composition, structure and crystalline phases.
Materials and Methods The enamel of 30 human deciduous teeth was examined by: Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray Spectroscopy (EDS), X-ray Powder Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), and X-ray Photoelectron Spectroscopy (XPS). Chemical differences between incisors and canines were statistically evaluated using the Mann-Whitney U test (p <= 0.05).
Results Three enamel patterns were observed by SEM: mostly smooth with some groves, abundant microporosities and exposed prisms. The average Ca/P molar ratios were 1.37 and 1.03 by EDS and XPS, respectively. The crystallite size determined by XRD was 210.82 +/- 16.78 angstrom. The mean ratio between Ca bonded to phosphate and Ca bonded to hydroxyl was approximately 10:1.
Conclusion The enamel of sound deciduous teeth showed two main patterns: mostly smooth with some groves and abundant microporosities. Exposed prisms was a secondary pattern. There were slight variations among the Ca/P molar ratios found by EDS and XPS, suggesting differences in the mineral content from the enamel surface to the interior. The crystalline phases found in enamel were hydroxyapatite and carbonate apatite, with major type B than type A carbonate incorporation.