A dimorphic magnetorheological elastomer incorporated with Fe nano-flakes modified carbonyl iron particles: preparation and characterization

作者：Yu M^*; Zhu M; Fu J; Yang P A; Qi S

来源：Smart Materials and Structures, 2015, 24(11): 115021.

DOI：10.1088/0964-1726/24/11/115021

• CIP-Nano-Fe
• magnetorheological elastomers
• magnetorheological properties
• damping properties

This paper describes a simple and convenient approach for the synthesis of Fe nano-flakes coated spherical carbonyl iron particles (CIP-Nano-Fe). The morphology and composition of CIP-Nano-Fe were characterized using electron scanning microscope and x-ray diffraction analysis. The results indicated that the CI particles were coated with uniform and continuous Fe nanostructures. Partial substitution of CI particles with CIP-Nano-Fe constituted a novel dimorphic magnetorheological elastomer (D-MRE), and the influence of the content of CIP-Nano-Fe on the viscoelastic performance of the magnetorheological elastomers (MREs) were systematically studied. The magnetorheological properties and the damping properties of the D-MRE samples were analyzed to evaluate their dynamic properties. The experimental results indicated that the MR effect, the max loss factor and the magneto-induced loss factor in the sample 3 (CIP-Nano-Fe weight content 6 wt%) were approximately 1.32, 1.45 and 1.56 times that in the sample 1 (non-doped MRE). The approach to synthesize CIP-Nano-Fe reported here can be readily explored for fabricating particles modified by other metal nanostructures, and the resulting D-MREs are expected to be applied in various applications, especially in the field of vibration and noise control, involving vibration isolators, tunable engine mounts, noise insulation devices, and so forth.

• 出版日期2015-11
• 单位重庆大学