A novel efficient halogen-free flame retardant system for polycarbonate

作者：Hu, Zhi; Chen, Li; Zhao, Bin; Luo, Yuan; Wang, De-Yi; Wang, Yu-Zhong^*

来源：Polymer Degradation and Stability, 2011, 96(3): 320-327.

DOI：10.1016/j.polymdegradstab.2010.03.005

• Polycarbonate
• Organic-inorganic hybrid
• MMT, flame retardant
• Cone calorimeter

A novel silicon- and phosphorus-containing flame retardant, poly (9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide siloxane), P(DOPO-VTES) was synthesized from 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide(DOPO) and vinyltriethoxy silane(VTES). Its chemical structure was confirmed by FTIR. The thermal gravimetrical analysis (TGA) showed that P(DOPO-VTES) had good thermal stability and a high of char yield (86.31%) at 700 degrees C in nitrogen atmosphere. Its XRD patterns showed that this compound had a certain ordered structure. P(DOPO-VTES) was blended with polycarbonate (PC) together with montmorillonite(MMT) to prepare a series of organic-inorganic hybrids of flame retardant (PC)/P (DOPO-VTES)/MMT via melt blending. The thermal degradation behavior and flame retardancy of those hybrids were investigated with TGA, limiting oxygen index (LOI), vertical burning test (UL-94), and cone calorimeter. The LOI value of the flame-retardant PC systems could reach a maximal value of 32.8 when the content of P(DOPO-VTES) was 5 wt%. When 2 wt% MMT was added into the PC/5%P(DOPO-VTES) system, the UL-94 rating reached V-0. The possible flame retardant mode of MMT was studied via the dynamic rheological properties of the systems and the morphology of the chars remaining after the LOI test and the cone calorimeter test.

• 出版日期2011-3
• 单位四川大学; 高分子材料工程国家重点实验室