Abnormal Grain Growth in Austenite Structure Reversely Transformed from Ferrite/Pearlite-Banded Structure

作者：Zhang Xianguang^*; Matsuura Kiyotaka; Ohno Munekazu

来源：Metallurgical and Materials Transactions A-Physical Metallurgy and Materials Science, 2014, 45A(10): 4623-4634.

DOI：10.1007/s11661-014-2364-4

The grain growth behavior of austenite reversely transformed from ferrite/pearlite (F/P)-banded and non-banded steels has been studied. It was found that the grain-coarsening temperature [the temperature at which abnormal grain growth (AGG) occurs] of the initially banded F/P structure is quite low compared with that of the non-banded sample. In the F/P-banded sample, the abnormal grains always originate from the former ferrite region. The occurrence of AGG is essentially attributable not to the austenite nucleation process during heating but to the grain growth process after the completion of austenizing. It was proposed that the lowered grain-coarsening temperature in the banded structure is due to the non-uniform pinning-effect of AlN precipitates between former ferrite and pearlite regions.

• 出版日期2014-9