Ultrasmall Dispersible Crystalline Nickel Oxide Nanoparticles as High-Performance Catalysts for Electrochemical Water Splitting

作者：Fominykh Ksenia^*; Feckl Johann M; Sicklinger Johannes; Doeblinger Markus; Boecklein Sebastian; Ziegler Juergen; Peter Laurence; Rathousky Jiri; Scheidt Ernst Wilhelm; Bein Thomas; Fattakhova Rohlfing Dina

来源：Advanced Functional Materials, 2014, 24(21): 3123-3129.

DOI：10.1002/adfm.201303600

• electrocatalysis
• nickel oxide
• nanocrystals
• solvothermal synthesis
• water splitting

Ultrasmall, crystalline, and dispersible NiO nanoparticles are prepared for the first time, and it is shown that they are promising candidates as catalysts for electrochemical water oxidation. Using a solvothermal reaction in tert-butanol, very small nickel oxide nanocrystals can be made with sizes tunable from 2.5 to 5 nm and a narrow particle size distribution. The crystals are perfectly dispersible in ethanol even after drying, giving stable transparent colloidal dispersions. The structure of the nanocrystals corresponds to phase-pure stoichiometric nickel(ii) oxide with a partially oxidized surface exhibiting Ni(iii) states. The 3.3 nm nanoparticles demonstrate a remarkably high turn-over frequency of 0.29 s-1 at an overpotential of g = 300 mV for electrochemical water oxidation, outperforming even expensive rare earth iridium oxide catalysts. The unique features of these NiO nanocrystals provide great potential for the preparation of novel composite materials with applications in the field of (photo)electrochemical water splitting. The dispersed colloidal solutions may also find other applications, such as the preparation of uniform hole-conducting layers for organic solar cells.

• 出版日期2014-6