As medium-strength steels are promising candidates for the hydrogen economy, it is important to understand their interaction with hydrogen. However, there are only a limited number of investigations on the behavior of medium-strength steels in hydrogen. The existing literature indicates that the influences of hydrogen on the tensile properties of medium-strength steels are mainly the following: (i) the steel can be hardened by hydrogen, as demonstrated by an increase in the yield stress or ultimate tensile stress; (ii) some steels can be embrittled by hydrogen, as revealed by lower yield stress or ultimate tensile stress; (iii) in most cases, these steels may experience hydrogen embrittlement (HE), as indicated by a reduction in ductility. The degree of HE mainly depends on the test conditions and the steel. The embrittlement can lead to catastrophic brittle fracture in service. The influence of hydrogen on the fatigue properties of medium-strength steels is dependent on many factors such as the stress ratio, temperature, yield stress of the steel, and test frequency. Generally, the hydrogen influence on fatigue limit is small, whereas hydrogen can accelerate the fatigue crack growth rate, leading to a shorter fatigue life. Inclusions are an important factor influencing the properties of medium-strength steels in the presence of hydrogen. However, it is not possible to predict the influence of hydrogen for any particular steel that has not been experimentally evaluated or to predict service performance. It is not known why similar steels can have different behavior, ranging from good resistance to significant embrittlement. A better understanding of the microstructural characteristics is needed.
- 出版日期2013-12