A Nanocrystalline POM@MOFs Catalyst for the Degradation of Phenol: Effective Cooperative Catalysis by Metal Nodes and POM Guests

作者：Zhong, Xiahua; Lu, Ying^*; Luo, Fang; Liu, Yiwei; Li, Xiaohui; Liu, Shuxia^*

来源：Chemistry - A European Journal, 2018, 24(12): 3045-3051.

DOI：10.1002/chem.201705677

• cooperative catalysis
• degradation of phenol
• liquid-assisted grinding
• nanocrystal
• POM-based MOFs

Crystalline POM@MOFs hybrids are very promising for catalysis, due to catalytically active polyoxometalates (POMs) dispersed at the molecular level, and enhanced stability of both POMs and metal-organic frameworks (MOFs). Herein, PW12 was encapsulated into MOF HKUST-1 through a facile liquid-assisted grinding method, and the obtained [Cu-2(BTC)(4/3)(H2O)(2)](6)[HPW12O40] (BTC = 1,2,3-benzenetricarboxylic acid) nanocrystals (NENU-3N) were applied as catalysts in the degradation of phenol. It is the first time that liquid-assisted grinding was applied in the preparation of nano-crystalline POM@MOFs hybrids. The NENU-3N nanocrystals catalyzed the degradation of phenol on the basis of both MOF and POM catalytic activities, representing the first example of POM@MOFs catalyst boosting catalytic oxidation reaction with double actives sites. Strikingly, up to 97% conversion and 88% mineralization have successfully realized by perfect cooperative catalysis between POMs and Cu-II nodes in MOFs at 35 degrees C. Moreover, comparative experiments suggest that the reduced size of NENU-3N catalyst is beneficial for improving its catalytic performance. Finally, the nanocrystalline NENU-3N catalyst possesses high stability, which can be easily recovered and reused 5 times without loss of catalytic activity.

• 出版日期2018-2-26
• 单位东北师范大学