A Facile Synthesis of ZnCo2O4 Nanocluster Particles and the Performance as Anode Materials for Lithium Ion Batteries

作者：Pan, Yue; Zeng, Weijia; Li, Lin; Zhang, Yuzi; Dong, Yingnan; Cao, Dianxue; Wang, Guiling^*; Lucht, Brett L.^*; Ye, Ke; Cheng, Kui

来源：Nano-Micro Letters, 2017, 9(2): 20.

DOI：10.1007/s40820-016-0122-4

• ZnCo2O4 nanocluster particles
• Hydrothermal method
• Sodium dodecyl benzene sulfonate
• Lithium ion batteries

ZnCo2O4 nanocluster particles (NCPs) were prepared through a designed hydrothermal method, with the assistance of a surfactant, sodium dodecyl benzene sulfonate. The crystalline structure and surface morphology of ZnCo2O4 were investigated by XRD, XPS, SEM, TEM, and BET analyses. The results of SEM and TEM suggest a clear nanocluster particle structure of cubic ZnCo2O4 (similar to 100 nm in diameter), which consists of aggregated primary nanoparticles (similar to 10 nm in diameter), is achieved. The electrochemical behavior of synthesized ZnCo2O4 NCPs was investigated by galvanostatic discharge/charge measurements and cyclic voltammetry. The ZnCo2O4 NCPs exhibit a high reversible capacity of 700 mAh g(-1) over 100 cycles under a current density of 100 mA g(-1) with an excellent coulombic efficiency of 98.9% and a considerable cycling stability. This work demonstrates a facile technique designed to synthesize ZnCo2O4 NCPs which show great potential as anode materials for lithium ion batteries.

• 出版日期2017-4
• 单位哈尔滨工程大学