Antiferromagnetism of LnRhO(3) (Ln = rare earth)

作者：Ohnishi T; Taniguchi T; Ikoshi A; Mizusaki S; Nagata Y^*; Lai S H; Lan M D; Noro Y; Ozawa T C; Kindo K; Matsuo A; Takayanagi S

来源：Journal of Alloys and Compounds, 2010, 506(1): 27-32.

DOI：10.1016/j.jallcom.2010.07.004

• Rhodium oxide
• Antiferromagnetism
• Rare-earth ion
• Metamagnetic transition
• Superexchange interaction

The crystallographic and magnetic properties of perovskite-type rhodite LnRhO(3) (Ln = rare-earth ions except Ce and Pm) were studied. LnRhO(3) (Ln = La, Eu, Lu) shows paramagnetism with very small susceptibility, suggesting that the Rh3+ ion has no magnetic moment. LnRhO(3) (Ln = Nd, Sm, Gd, Tb, Dy, Ho, Er, Yb) shows antiferromagnetic transition at temperatures between 0.5 and 3.5 K; however, no transition was observed for LnRhO(3) (Ln = Pr, Tm) down to 0.5K. The effective moment mu(eff) agrees with the theoretical moment of free rare-earth ions, indicating the dominant magnetic contribution of rare-earth ions. The Weiss temperature Theta has a strong correlation with the spin value of rare-earth ions, suggesting that the superexchange interaction is a dominant interaction in LnRhO(3). The magnetization of antiferromagnetic samples tends to be saturated above 20-30 kOe, but the moments at 70 kOe are far from the theoretical moments. Antiferromagnetic samples seem to have an intermediate state and require a more intense magnetic field to attain saturation.

• 出版日期2010-9-10