Tin oxide (SnO2) nanotubes with a fiber-in-tube structure have been prepared by electrospinning and the mechanism of their formation has been investigated. Tin oxide-carbon composite nanofibers with a filled structure were formed as an intermediate product, which were then transformed into SnO2 nanotubes with a fiber-in-tube structure during heat treatment at 500 degrees C. Nanofibers with a diameter of 85 nm were found to be located inside hollow nanotubes with an outer diameter of 260 nm. The prepared SnO2 nanotubes had well-developed mesopores. The discharge capacities of the SnO2 nanotubes at the 2nd and 300th cycles at a current density of 1 Ag-1 were measured as 720 and 640 mAhg(-1), respectively, and the corresponding capacity retention measured from the 2nd cycle was 88%. The discharge capacities of the SnO2 nanotubes at incrementally increased current densities of 0.5, 1.5, 3, and 5 Ag-1 were 774, 711, 652, and 591 mAhg(-1), respectively. The SnO2 nanotubes with a fiber-in-tube structure showed superior cycling and rate performances compared to those of SnO2 nanopowder. The unique structure of the SnO2 nanotubes with a fiber@void@tube configuration improves their electrochemical properties by reducing the diffusion length of the lithium ions, and also imparts greater stability during electrochemical cycling.
- 出版日期2015-1-2