Mechanical failure and glass transition in metallic glasses

作者：Egami T^*

来源：Journal of Alloys and Compounds, 2011, 509: S82-S86.

DOI：10.1016/j.jallcom.2010.11.007

• Metallic glasses
• Mechanical deformation
• Glass transition
• Defects

The current majority view on the phenomenon of mechanical failure in metallic glasses appears to be that it is caused by the activity of some structural defects, such as free-volumes or shear transformation zones, and the concentration of such defects is small, only of the order of 1%. However, the recent results compel us to revise this view. Through molecular dynamics simulation it has been shown that mechanical failure is the stress-induced glass transition. According to our theory the concentration of the liquid-like sites (defects) is well over 20% at the glass transition. We suggest that the defect concentration in metallic glasses is actually very high, and percolation of such defects causes atomic avalanche and mechanical failure. In this article we discuss the glass transition, mechanical failure and viscosity from such a point of view.

• 出版日期2011-6