摘要
The evaluation of local mechanical properties of metal parts can be used for the prediction of forming and cutting forces during the following working stages. In order to show the feasibility of using indentation tests for work-piece characterization, C40 steel disks were cut from an extruded bar and machined by facing operation under different conditions. Indentation tests were carried out with 1 mm and 2 mm diameter indenters made of tungsten carbide: yield strength and indentation pressure values were extracted along the diameter of each disk. For the first time, indentation results were used to extract local mechanical properties of steel bars as a function of their process conditions: it was observed that small pins gave information on the effect of the machining process whereas large pins were more suitable to evaluate work-piece bulk properties.