Nitrogen-doped TiO2(B) nanorods as high-performance anode materials for rechargeable sodium-ion batteries

作者：Yang, Yingchang^*; Liao, Shijia; Shi, Wei; Wu, Yundong; Zhang, Renhui; Leng, Senlin^*

来源：RSC Advances, 2017, 7(18): 10885-10890.

DOI：10.1039/c7ra00469a

• ANATASE TIO2
• RUTILE TIO2
• LI-ION
• STORAGE
• NANOPARTICLES
• LITHIUM
• NANOFIBERS
• NANOTUBES
• COMPOSITE
• HYBRID

To achieve better anode materials for sodium ion batteries, a nitrogen-doped TiO2(B) nanorod structure is developed utilizing hydrothermal treatment, ion exchange and a subsequent low temperature calcination process. Transmission electron microscopy, X-ray photoelectron spectroscopy and X-ray diffraction are employed to characterize the structure and properties of the nitrogen-doped TiO2(B). Compared with anatase TiO2 powder (325 mesh) raw materials and the TiO2(B) nanorods without N-doping, the asfabricated nitrogen-doped TiO2(B) nanorods with a nitrogen-doping amount of 1.23 atom% exhibit higher specific capacity (224.5 mA h g(-1)), good cycling stability (the capacity retention ratios after 200 cycles at 2C is 93.4%) and enhanced rate capability (110 mA h g(-1) at 3.35 A g(-1)), which is likely to be associated with enhanced conductivity due to N-doping.

• 出版日期2017
• 单位铜仁学院