The hot ductility of Nb/V containing high Al, TWIP steels

作者：Kang S E; Tuling A; Lau I; Banerjee J R; Mintz B^*

来源：Materials Science and Technology, 2011, 27(5): 909-915.

DOI：10.1179/026708309X12595712305915

• Hot ductility
• TWIP steels
• High Al
• Nb and V
• Cooling rate
• Transverse cracking

The hot ductility of Nb/V containing high Al, twin induced plasticity (TWIP) steels has been examined over the temperature range 650-1150 degrees C after melting and after 'solution treatment'. Previous work had shown that the hot ductility is poor for the 1.5 mass-%Al, TWIP steel due to precipitation of AlN at the austenite grain boundaries, the depth of the trough being similar to that for an X65 grade pipeline steel but with the trough covering a much wider temperature range. Adding Nb and V made the ductility even worse due to the additional precipitation of NbCN and VN. Very low reduction of area values, 10-20% were obtained in the temperature range 700-900 degrees C. Increasing the cooling rate to the test temperature resulted in even worse ductility. The ductility of these steels after 'solution treatment' is similar to that obtained after melting but when the cast was hot rolled followed by 'solution treatment' and cooling to the test temperature ductility improved due to grain refinement.

• 出版日期2011-5