A DFT study on the failure mechanism of Al2O3 film by various point defects in solution

作者：Zhang, Chuan-Hui^*; Chen, Bao; Jin, Ying; Sun, Dong-Bai

来源：Chemical Physics, 2018, 504: 48-56.

DOI：10.1016/j.chemphys.2018.02.026

• Point defect
• Al2O3 film
• H2O dissociation

The defects on oxide film surface are very important, and they would occur when the film is peeled or scratched. The periodic DFT calculations have been performed on Al2O3 surface to model the influences of various point-defects. Three kinds of point defect surfaces (vacancy, inversion, substitution) are considered, and the molecular H2O dissociation and the transition state are calculated. The predicted formation energy of O vacancy is 8.30 eV, whereas that corresponding to the formation of Al vacancy is found to be at least a 55% larger. On the vacancy point defect surfaces, upward H2O molecule surfaces prefer to occur chemical reaction, leading the surfaces to be hydroxylated. And then the D-Cl-substitution-Al surface is corroded, which suggests a Cl adsorption induced failure mechanism of the oxide film. At last, the process of H2O dissociation on the OH-substitution-Al surfaces with four or five transition paths are discussed.

• 出版日期2018-3-26
• 单位北京科技大学