Structural and physicochemical properties of nickel manganite NiMn2O4-delta synthesized by sol-gel and ultra sound assisted methods

作者：Alburquenque D; Troncoso L; Denardin J C; Butera A; Padmasree K D; Ortiz J; Herrera F; Marco J F; Gautier J L^*

来源：Journal of Alloys and Compounds, 2016, 672: 307-316.

DOI：10.1016/j.jallcom.2016.02.090

• Nickel manganite
• Spinel oxides
• Magnetic properties
• X-ray diffraction
• XPS

In this work we present the structural, magnetic and surface characterization of the ceramic nickel manganite oxide NiMn2O4-delta synthesized by two methods: sol-gel and ultrasound-assisted sol-gel using nitrate salts as precursors. We have characterized the non-stoichiometric samples NiMn2O4-delta using different physicochemical analyses. X-ray diffraction and Rietveld refinement of the X-ray data indicated that the samples crystallize in the Fd3m space group characteristic of cubic spinel-related oxides. The specific surface area of the oxides was 1.3 m(2)/g (SG) and 16.3 m(2)/g (UASG). SEM results showed particle agglomerates of 1.05 mu m ( SG) and 0.85 mu m ( UASG). Temperature dependence magnetization measurements were performed and a ferrimagnetic transition was identified at 103 K and 105 K depending on the preparation method ( SG and UASG, respectively). The observed Curie constant was found to vary from 7.4 to 7.7 cm(3) K mol(-1) and hysteretic magnetization vs. applied field curves at different temperatures were obtained. XPS studies of these oxides reveal the presence of Ni2+, Mn2+, Mn3+ and Mn4+ ions at the surface. A probable ionic distribution as a function of the synthesis method is proposed.

• 出版日期2016-7-5