Microstructure evolution and coercivity enhancement in Nd-Fe-B thin films diffusion-processed by R-Al alloys (R=Nd, Pr)

作者：Xie, Yigao; Yang, Yang; Zhang, Tongbo; Fu, Yanqing; Jiang, Qingzheng; Ma, Shengcan; Zhong, Zhenchen; Cui, Weibin^*; Wang, Qiang

来源：AIP Advances, 2018, 8(5): 056202.

DOI：10.1063/1.5006110

• ELECTROPHORETIC DEPOSITION
• TBF3 DIFFUSION
• MAGNETS

Diffusion process by Nd-Al and Pr-Al alloys was compared and investigated in Nd-Fe-B thin films. Enhanced coercivity 2.06T and good squareness was obtained by using Pr85Al15 and Nd85Al15 alloys as diffusion sources. But the coercivity of diffusion-processed thin films by Pr70Al30 and Pr55Al45 alloys decreased to 2.04T and 1.82T. High ambient coercivity of 2.26T was achieved in diffusion-processed thin film by Nd70Al30 leading to an improved coercivity thermal stability because Nd2Fe14B grains were enveloped by Nd-rich phase as seen by transmission electron microscopy Nd-loss image. Meanwhile, microstructure-dependent parameters alpha and N-eff were improved. However, high content of Al in diffusion- processed thin film by Nd55Al45 lead to degraded texture and coercivity.

• 出版日期2018-5
• 单位东北大学; 江西理工大学