Size and Spatial Distribution of Micropores in SBA-15 using CM-SANS

作者：Pollock Rachel A; Walsh Brenna R; Fry Jason; Ghampson I Tyrone; Melnichenko Yuri B; Kaiser Helmut; Pynn Roger; DeSisto William J; Wheeler M Clayton; Frederick Brian G^*

来源：Chemistry of Materials, 2011, 23(17): 3828-3840.

DOI：10.1021/cm200707y

• mesoporous silica
• SBA-15
• neutron scattering
• micropore structure

Diffraction intensity analysis of small-angle neutron scattering measurements of dry SBA-15 have been combined with nonlocal density functional theory (NLDFT) analysis of nitrogen desorption isotherms to characterize the micropore, secondary mesopore, and primary mesopore structure. The radial dependence of the scattering length density, which is sensitive to isolated surface hydroxyls, can only be modeled if the NLDFT pore size distribution is distributed relatively uniformly throughout the silica framework, not localized in a "corona" around the primary mesopores. Contrast matching-small angle neutron scattering (CM-SANS) measurements, using water, decane, tributylamine, cyclohexane, and isooctane as direct probes of the size of micropores indicate that the smallest pores in SBA-15 have diameter between 5.7 and 6.2 angstrom. Correlation of the minimum pore size with the onset of the micropore size distribution provides direct evidence that the shape of the smallest micropores is cylinderlike, which is consistent with their being due to unraveling of the polymer template.

• 出版日期2011-9-13