In vitro study on the degradation of lithium-doped hydroxyapatite for bone tissue engineering scaffold

作者：Wang, Yaping; Yang, Xu; Gu, Zhipeng; Qin, Huanhuan; Li, Li; Liu, Jingwang; Yu, Xixun^*

来源：Materials Science & Engineering C-Materials for Biological Applications, 2016, 66: 185-192.

DOI：10.1016/j.msec.2016.04.065

• Li-doped hydroxyapatite (LiHA) scaffolds
• In vitro solution-mediated degradation
• In vitro osteoblast-mediated degradation
• Bioactivity
• Bone tissue engineering

Li-doped hydroxyapatite (LiHA) which is prepared through introducing low dose of Li into hydroxyapatite (HA) has been increasingly studied as a bone tissue-engineered scaffold. The degradation properties play a crucial role in the success of long-term implantation of a bone tissue-engineered construct. Herein, the in vitro degradation behaviors of LiHA scaffolds via two approaches were investigated in this study: solution-mediated degradation and osteoblast-mediated degradation. In solution-mediated degradation, after being immersed in simulated body fluid (SBF) for some time, some characteristics of these scaffolds (such as release of ionized lithium and phosphate, pH change, mechanical properties, cytocompatibility and SEM surface characterization) were systematically tested. A similar procedure was also employed to research the degradation behaviors of LiHA scaffolds in osteoblast-mediated degradation. The results suggested that the degradation in SBF and degradation in culture medium with cell existed distinguishing mechanisms. LiHA scaffolds were degraded via a hydrolytic mechanism when they were soaked in SBF. Upon degradation, an apatite precipitation (layer) was formed on the surfaces of scaffolds. While a biological mechanism was presented for the degradation of scaffolds in cell-mediated degradation. Compared with pure HA, LiHA scaffolds had a better effect on the growth of osteoblast cells, meanwhile, the release amount of PO43- in a degradation medium indicated that osteoblasts could accelerate the degradation of LiHA due to the more physiological activities of osteoblast. According to the results from compressive strength test, doping Li into HA could enhance the strength of HA. Moreover, the results from MIT assay and SEM observation showed that the degradation products of LiHA scaffolds were beneficial to the proliferation of osteoblasts. The results of this research can provide the theoretical basis for the clinical application of LiHA scaffolds.

• 出版日期2016-9-1
• 单位四川大学