Adhesion Characteristics of a Novel Synthetic Polydimethylsiloxane for Bionic Adhesive Pads

作者：He Qingsong; Yu Min; Li Yang; Chen Xinlong; Zhang Hao; Gong Ling; Dai Zhendong^*

来源：Journal of Bionics Engineering, 2014, 11(3): 371-377.

DOI：10.1016/S1672-6529(14)60050-0

• polymeric composite
• adhesion
• carbon materials
• surface energy
• bionic

Materials with appropriate adhesive properties are suitable for the fabrication of bionic adhesive pads. In this study, a novel polydimethylsiloxane (PDMS) material enhanced with two types of crosslinkers, carbon nanotubes and graphene sheets, was fabricated. The Contact Angle (CA) and cross-sectional morphology of the new material were investigated and observed using a CA meter and Scanning Electron Microscopy (SEM), respectively. CA measurements indicate that the surface energy of the novel material is twice that of the common PDMS material. SEM observations show that carbon nanotubes and graphene sheets are well dispersed in the polymer, a feature that improves the mechanical properties of the new material. The adhesive performance of this novel composite was tested on an in-house fabricated friction machine. Results show that at a preload of only 50 mN, the adhesion of the novel PDMS material is up to similar to 3.7 times that of common PDMS. The maximum macroscale shear strength and normal adhesion reach 4 N.cm(-2) and 1 N.cm(-2), respectively. The adhesive capability of the material is maintained even after hundreds of times of repeated use. This novel material exhibits excellent adhesion, sufficiently high elastic modulus and high repeatability at low preloads.

• 出版日期2014-7
• 单位南京航空航天大学; 中国空间技术研究院