Direct preparation of high surface area mesoporous SiC-based ceramic by pyrolysis of a self-assembled polycarbosilane-block-polystyrene diblock copolymer

作者：Nghiem Quoc Dat; Kim Dong Pyo^*

来源：Chemistry of Materials, 2008, 20(11): 3735-3739.

DOI：10.1021/cm702688j

Direct pyrolysis of a self-assembled inorganic-organic block copolymer can be a promising route for fabricating the ordered ceramic nanostructures based on the achievements of organic-organic block copolymers. Here we report the synthesis of a novel polycarbosilane-block-polystyrene diblock copolymer by ring-opening living anionic polymerization in a THF and n-hexane solvent system at similar to 48 degrees C. The resulting block copolymer revealed phase-separation behavior in the nanoscale to form a self-assembled nanostructure that was converted to a mesoporous ceramic phase after heating at 800 degrees C. The pyrolyzed ceramic product exhibited well-ordered mesoporous SiC-based ceramic structures with a high BET surface area of 1325 m(2) g(-1) and an average mesopore size of 7.8 nm containing a large amount of micropores.

• 出版日期2008-6-10