Fabrication of Aluminum Foams with Small Pore Size by Melt Foaming Method

作者：Cheng, Ying; Li, Yanxiang^*; Chen, Xiang; Shi, Tong; Liu, Zhiyong; Wang, Ningzhen

来源：Metallurgical and Materials Transactions B-Process Metallurgy and Materials Processing Science, 2017, 48(2): 754-762.

DOI：10.1007/s11663-016-0815-6

• MANUFACTURE
• TIH2

This article introduces an improvement to the fabrication of aluminum foams with small pore size by melt foaming method. Before added to the melt, the foaming agent (titanium hydride) was pretreated in two steps. It firstly went through the traditional pre-oxidation treatment, which delayed the decomposition of titanium hydride and made sure the dispersion stage was controllable. Then such pre-oxidized titanium hydride powder was mixed with copper powder in a planetary ball mill. This treatment can not only increase the number of foaming agent particles and make them easier to disperse in the melt, which helps to increase the number of pores, but also reduce the amount of hydrogen released in the foaming stage. Therefore, the pore size could be decreased. Using such a ball-milled foaming agent in melt foaming method, aluminum foams with small pore size (average size of 1.6 mm) were successfully fabricated.

• 出版日期2017-4
• 单位清华大学