Anionic Copolymerization Enables the Scalable Synthesis of Alternating (AB)(n) Multiblock Copolymers with High Molecular Weight in n/2 Steps

作者：Grune Eduard; Appold Michael; Mueller Axel H E; Gallei Markus; Frey Holger^*

来源：ACS Macro Letters, 2018, 7(7): 807-810.

DOI：10.1021/acsmacrolett.8b00390

Based on the highly disparate reactivities of isoprene (I, r(I) = 25.4) and 4-methylstyrene (4MS, r(4MS) = 0.007) in the anionic copolymerization in nonpolar media, a general strategy for the rapid and scalable synthesis of tapered multiblock copolymers with an extremely steep gradient has been developed, A repetitive addition strategy of a mixture of isoprene and 4MS leads to a tapered diblock in each case, giving access to linear alternating multiblock copolymers of the (AB)(n) type with up to 10 blocks. All multiblock copolymers showed narrow molecular weight distributions (dispersity D = 1.04-1.12). High molecular weights in the range of 80 to 400 kg mol(-1) were achieved. Due to the incompatibility of PI and P4MS segments, the multiblock copolymers exhibit nanophase separation, manifested by separate glass transitions for both constituents. Stress-strain measurements revealed extraordinary toughness and elongations up to 1150% strain at break, even at a 50/50 molar ratio I/4MS (i.e., 37 wt% isoprene). Our synthesis permits access to a wide range of tapered multiblock copolymer architectures with rigid (P4MS, high glass transition, T-g) and flexible (low T-g) chains, in n/2 steps, while keeping overall dispersity low.

• 出版日期2018-7