Graphitization of nanocrystalline carbon microcoils synthesized by catalytic chemical vapor deposition

作者：Bi Hui^*; Kou Kai Chang; Ostrikov Kostya; Zhang Jiao Qiang

来源：Journal of Applied Physics, 2008, 104(3): 033510.

DOI：10.1063/1.2963712

Graphitization, a common process involving the transformation of metastable nongraphitic carbon into graphite is one of the major present-day challenges for micro- and nanocarbons due to their unique structural character and highly unusual thermal activation. Here we report on the successful graphitization of nanocrystalline carbon microcoils prepared by catalytic chemical vapor deposition and post-treated in argon atmosphere at temperatures similar to 2500 degrees C for 2 h. The morphology, microstructure, and thermal properties of the carbon microcoils are examined in detail. The graphitization mechanism is discussed by invoking a model of structural transformation of the carbon microcoils. The results reveal that after graphitization the carbon microcoils are prominently purified and feature a clear helical morphology, as well as a more regular and ordered microstructure. The interlayer spacing of the carbon microcoils decreases from 0.36 to 0.34 nm, whereas the mean crystal sizes in the c- and a-directions increase from 1.64 to 2.04 nm and from 3.86 to 7.21 nm, respectively. Thermal treatment also substantially improves the antioxidation properties of the microcoils by lifting the oxidation onset temperature from 550 to 672 degrees C. This process may be suitable for other nongraphitic micro- and nanomaterials.

• 出版日期2008-8-1
• 单位西北工业大学; CSIRO