A simple, template-free route for the synthesis of mesoporous titanium dioxide materials

作者:Liu CQ*; Lei FB; Economy J
来源:Journal of Materials Chemistry, 2004, 14(7): 1187-1189.
DOI:10.1039/b316426h

摘要

Mesoporous titanium dioxide (TiO2) materials have been synthesized by a novel simple, template-free synthetic approach, which was carried out via nitric acid-catalyzed hydrolysis and polycondensation reactions of titanium(IV) n-butoxide. The as-prepared and calcinated mesoporous TiO2 materials are characterized by X-ray diffraction (XRD), transmission electron microscope (TEM), and N-2 adsorption/ desorption measurements. The as-prepared amorphous TiO2 possesses a high BET surface area of 470 m(2) g(-1) and a pore volume of 0.28 cm(3) g(-1). After calcinations at 450 degreesC, anatase mesoporous TiO2 is formed with a BET surface area of 106 m(2) g(-1) and an average pore size of 4.8 nm. Avoidance of the structure-directing template during the synthesis of mesoporous TiO2 is of significant importance for application from both environmental and industrial points of view.