Morphological and physical properties and friction/wear behavior of h-BN filled PEEK composite coatings

作者：Tharajak Jirasak; Palathai Tippaban^*; Sombatsompop Narongrit

来源：Surface and Coatings Technology, 2015, 273: 20-29.

DOI：10.1016/j.surfcoat.2015.03.030

• Flame-spray coating technique
• Polyether ether ketone (PEEK)
• Hexagonal boron nitride
• Solid lubricant
• Tribology

Hexagonal boron nitride (h-BN) powder with different particle sizes and contents was incorporated in polyether ether ketone (PEEK) under ultrasonic conditions and deposited using flame-spray coating technique. Specific wear rate and friction coefficient of the h-BN/PEEK composite coatings were determined using a ball-on-disk sliding wear tester under applied loads of 5-25 N. Microstructure, microhardness, degree of crystallinity and surface roughness of the h-BN/PEEK composite coatings were investigated. The results showed that the microhardness and degree of crystallinity could be improved with h-BN particles. At an applied load of 5 N, the addition of h-BN particles into PEEK gave a lower specific wear rate. A higher content of h-EN added to PEEK coating resulted in a decrease in the friction coefficient. At an applied load of 25 N, 8 wt.% h-BN/PEEK composite coatings provided good friction reduction while the composite coatings formed severe wear with grooves.

• 出版日期2015-7-15