Microstructures and Properties of W-Ti Alloys Prepared Under Different Cooling Conditions

作者：Dai, Weili^*; Liang, Shuhua^*; Yang, Qing; Zou, Juntao; Zhuo, Longchao

来源：Journal of Materials Engineering and Performance, 2016, 25(7): 2626-2634.

DOI：10.1007/s11665-016-2146-9

• cooling conditions
• decomposition
• properties
• sintering
• titanium phase
• W-Ti alloy

W-(10 to 15) wt.% Ti alloys were sintered at 1400 or 1500 A degrees C and cooled under different cooling conditions. The microstructures and properties of W-Ti alloys were affected by the cooling conditions. XRD, SEM, EBSD, and TEM were carried out to investigate the effects of cooling conditions and sintering temperature on the microstructures of W-Ti alloys. The nanohardness and elastic modulus of the alloys were also investigated. The results showed that when the temperature was 1500 A degrees C, the content of Ti-rich phase in W-(10 to 15) wt.% Ti alloys decreased obviously with the increase of cooling rate (the average cooling rate of furnace cooling, air cooling and water cooling was 0.2, 10, and 280 A degrees C/s, respectively). For the W-10 wt.% Ti alloy, the content decreased from 20.5 to 9.7%, and the grain size decreased from 2.33 to 0.67 mu m. When the temperature decreased to 1400 A degrees C, the grain size was also decreased sharply with the increase of cooling rate, but there was a little change in the microstructure. Meanwhile, the grain sizes were smaller than those of the alloys sintered at 1500 A degrees C. The nanohardness and elastic modulus increased with the increase of cooling rate, and the alloys sintered at different temperatures had different nanohardness and elastic modulus which depended on the cooling conditions. Sintering at a proper temperature and then cooling at a certain cooling condition was a useful method to fabricate alloy with less Ti-rich phase and high properties.

• 出版日期2016-7
• 单位西安理工大学