Melamine amino trimethylene phosphate as a novel flame retardant for rigid polyurethane foams with improved flame retardant, mechanical and thermal properties

作者：Liu, Lei; Wang, Zhengzhou^*; Xu, Xiaoyan

来源：Journal of Applied Polymer Science, 2017, 134(39): 45234.

DOI：10.1002/app.45234

• flame retardance
• microscopy
• thermogravimetric analysis (TGA)

Melamine amino trimethylene phosphate (MATMP) as a novel nitrogen-phosphorus flame retardant, was synthesized by the reaction of melamine with amino trimethylene phosphonic acid (ATMP) in aqueous solution. The structure of MATMP was characterized by Fourier transform infrared spectroscopy, solid state P nuclear magnetic resonance, and thermogravimetric analysis. Rigid polyurethane (RPU) foams were prepared by one-shot and free-rise method, using MATMP as a flame retardant. The flame retardant, mechanical and thermal properties of MATMP in RPU foams were studied. It is found that the RPU foam containing 15 wt % MATMP (sample RPUMA-15) can pass the UL-94 V0 test with a limiting oxygen index of 25.5%. The cone calorimeter test results show that the peak heat release rate of RPUMA-15 is reduced about 34% compared with that of untreated RPU foam. SEM results indicate that the RPU foams with MATMP can form the good and compact char during burning which provides better flame retardancy. The compressive strength of the RPU foams filled with MATMP first increases and then slightly decreases with an increase in the MATMP content comparing with that of untreated RPU foam. Moreover, thermal conductivities of the MATMP filled RPU foams are about 0.03 W/mK.

• 出版日期2017-10-15
• 单位同济大学