Grain refinement of AZ91D alloy by intensive melt shearing and its persistence after remelting and isothermal holding

作者：Zuo Yubo^*; Fan Zhongyun; Cui Jianzhong

来源：China Foundry, 2013, 10(1): 39-42.

• magnesium alloy
• microstructure
• intensive melt shearing
• remelting
• isothermal holding

Intensive melt shearing has a significant grain refining effect on some light alloys. However, the persistence of the grain refining effect during isothermal holding and remelting is still unclear, although it is very important for the practical application. In this study, intensive melt shearing was achieved in a twin-screw mechanism to investigate its grain refining effect on AZ91D magnesium alloy. The refinement mechanism was discussed and the persistence of grain refinement after remelting and isothermal holding was also studied. A Zeiss imaging system with polarized light was used for quantitative measurement of grain size. The results show that the intensive melt shearing has a significant grain refining effect on AZ91D magnesium alloy. With the application of intensive melt shearing, the grain size of AZ91D magnesium alloy can be reduced from 530 mu m (for a typical as-cast microstructure) to 170 mu m, which is about 70% size reduction. The grain refinement achieved by the intensive melt shearing can be partially kept after isothermal holding and remelting. It is believed that the refinement effect was mainly due to the finer and well dispersed oxide particles formed by high intensive shearing. The smaller size of oxide particles and their slow motion velocity in the sheared melt could make important contributions to the remained grain refinement.

• 出版日期2013-1
• 单位东北大学