Antibacterial effect and cytotoxicity of Ag-doped functionally graded hydroxyapatite coatings

作者：Bai Xiao; Sandukas Stefan; Appleford Mark; Ong Joo L; Rabiei Afsaneh^*

来源：Journal of Biomedical Materials Research Part B: Applied Biomaterials , 2012, 100B(2): 553-561.

DOI：10.1002/jbm.b.31985

• hydroxyapatite coatings
• antimicrobial
• antibacterial effect
• cytotoxicity

Functionally graded hydroxyapatite coatings (FGHA) doped with 1, 3, and 6.5 wt % silver (Ag) have been deposited on Titanium using ion-beam-assisted deposition. Scanning transmission electron microscopy on coating cross sections confirmed the presence of FGHA coating with mostly amorphous layers at the top and mostly crystalline layers toward the coating interface as well as the existence of 1050 nm Ag particles distributed throughout the thickness of the coatings. Calcium release in phosphate buffered saline solution showed a high release rate of Ca at the beginning of the test, and a gradual decrease in release rate thereafter to a minimum level until day 7. Similarly, the release rate of Ag in ultra pure water was initially high in the first 4 h and then gradually decreased over a 7 days period. Antibacterial tests have shown a reduction in the viability of S. aureus in Ag-doped coatings particularly in samples with higher Ag concentrations of 3 and 6.5 wt %. Cytotoxicity tests using an osteoblast cell line, on the other hand, have demonstrated that the samples with 6.5 wt % Ag have a negative effect on osteoblast cell response, proliferation, and apoptosis as well as a negative effect on protein and osteocalcin production. It is notable that the samples with 3 wt % Ag or less presented minimal cytotoxicity compared with control surfaces. Considering both the antibacterial and cytotoxicity effects, it is suggested that the 3 wt % of Ag in FGHA coatings can be favorable.

• 出版日期2012-2