Morphotropic phase boundary and electrical properties of lead-free bismuth sodium lanthanum titanate-barium titanate ceramics

作者：Pengpat K^*; Hanphimol S; Eitssayeam S; Intatha U; Rujijanagul G; Tunkasiri T

来源：Journal of Electroceramics, 2006, 16(4): 301-305.

DOI：10.1007/s10832-006-9869-1

• BNLT
• BT
• lead -free piezoelectric ceramic
• conventional ceramic method

The important properties of lead-free piezoelectric ceramics have been investigated from Bismuth Sodium Lanthanum Titanate and Barium Titanate system: (1 - y)(Bi0.5Na0.5)((1 - 1.5x))La (x) TiO3(BNLT)-yBaTiO(3)(BT) where x = 0.017 and y = 0 - 0.2, respectively. The morphotropic phase boundary (MPB) was found to be around y = 0.1 by the x-ray diffraction and dielectric measurement at various amount of BT. The temperature dependence of dielectric constant (epsilon(r) ) at various value of y showed the diffuse phase transition exhibiting the relaxor type ferroelectrics. The degree of diffuseness increased at a high doping content of about y = 0.15 where the second phase transition (T-2) of the ferroelectric to antiferroelectric phase disappeared. Moreover, this sample had the maximum piezoelectric coefficient (d(33)) of about 112 pC/N with relatively low dielectric constant. The optimum sintering temperatures and the microstructures of the dense BNLT-BT ceramics were also examined.

• 出版日期2006-7