Microstructural evolution of NbF(5)-doped MgH(2) exhibiting fast hydrogen sorption kinetics

作者：Kim Ji Woo; Ahn Jae Pyoung^*; Jin Seon Ah; Lee Sang Hoon; Chung Hee Suk; Shim Jae Hyeok; Cho Young Whan; Oh Kyu Hwan

来源：Journal of Power Sources, 2008, 178(1): 373-378.

DOI：10.1016/j.jpowsour.2007.12.005

• hydrogen storage
• hydrides
• transmission electron microscopy
• focused ion beam
• catalysts

The microstructure of MgH(2) with 1 mol% NbF(5), Prepared by high-energy ball milling (HEBM), was studied using high resolution transmission electron microscopy (HR-TEM) with an X-ray energy dispersive spectrometer (EDS) before and after hydrogen sorption cycles. The TEM samples were prepared without any air exposure by a novel, focused ion beam (FIB) system specially designed for highly air sensitive materials. During HEBM, the doping agent, NbF5, was distributed as an extremely thin, film-like, amorphous phase along the grain boundaries of the nanocrystalline MgH2. After 10 sorption cycles, amorphous Nb-F phase was transformed into crystalline Nb hydrides. It is believed that the Nb hydride played a decisive role in improving the sorption kinetics of MgH(2).

• 出版日期2008-3-15