Measurement of Young's modulus of oxides at high temperature related to the oxidation study

作者：Saeki Isao^*; Ohno Takuto; Seto Daigo; Sakai Ofuyu; Sugiyama Yusuke; Sato Tadao; Yamauchi Akira; Kurokawa Kazuya; Takeda Mikako; Onishi Takashi

来源：Materials at High Temperatures, 2011, 28(4): 264-268.

DOI：10.3184/096034011X13182685579795

• alpha-Al(2)O(3)
• Cr(2)O(3)
• alpha-Fe(2)O(3)
• Young's modulus
• sintering
• steels and heat-resistant alloys
• surface oxide film

alpha-Al(2)O(3), Cr(2)O(3), and alpha-Fe(2)O(3) specimens were prepared by a sintering process. A 400-1000-Hz sine wave was applied to the specimen at 290 -1273 K. The applied and respond waves were monitored by using force and acceleration sensors. The intensity ratio and phase shift between the applied and respond waves were analysed, and the anti-resonance frequency was obtained. Young's moduli of alpha-Al(2)O(3), Cr(2)O(3), and alpha-Fe(2)O(3) are estimated to be 386, 286, and 220 GPa at 298 K, respectively. The temperature dependence values of these oxides are estimated to be 54.3, 46.9, and 42.0 MPa K(-1), respectively. The temperature dependence of Young's modulus can be classified on the basis of the crystal structure of solids. The estimation of Young's modulus at 1273K is possible with an error range of 10-30 GPa for a crystalline solid if the crystal structure of the solid is known. It is found that the temperature dependence of Young's modulus depends on the density of the oxides, and an experiment in which well-characterized crystalline solids are used must be conducted to minimize the error range.

• 出版日期2011-11