Novel high-efficiency Eu3+-activated Na2Gd2B2O7red-emitting phosphors with high color purity????(Open Access)

作者：Sakthivel, Thangavel; Sun, Liangling; Devakumar, Balaji; Li, Bin; Huang, Xiaoyong^*

来源：RSC Advances, 2018, 8(57): 32948-32955.

DOI：10.1039/c8ra06607h

• Correlated color temperature
• Dipole dipole interactions
• High color rendering index
• Internal quantum efficiency
• Near ultraviolet excitations
• Non-radiative transitions
• Photo-luminescence excitation
• White light emitting diodes

In this study, a series of Na2(Gd1-xEux)2B2O7(abbreviated as: Na2Gd2B2O7:xEu3+;x = 0, 0.05, 0.15, 0.35, 0.45, and 0.50) phosphors were synthesized by conventional solid state reaction approach. The structure and morphology of the as-prepared phosphors were studied by X-ray diffraction, scanning electron microscopy and elemental mapping. The results indicated that the phosphors had micro-size particles with monoclinic phases. The photoluminescence excitation and emission study indicated that the as-prepared phosphors could give rise to efficient red emissions under near-ultraviolet excitation. The optimal doping concentration of Eu3+ions was x = 0.35, and the corresponding deduced critical distance (Rc) was about 9.4 Å. The concentration quenching mechanism was dominated by energy-transfer among the Eu3+ions through dipole-dipole interactions. The calculated internal quantum efficiency of the Na2Gd2B2O7:0.35Eu3+red phosphor was 70.8% and the color purity was as high as 99%. Furthermore, decay dynamics revealed that with the increase in the content of Eu3+, the lifetimes decreased due to the increase in non-radiative transition. Importantly, the present Na2Gd2B2O7:0.35Eu3+phosphors also exhibited good thermal stability, and the emission intensity at 150 °C was about 56% of that at 30 °C. Furthermore, a warm white light-emitting diode (WLED) device was fabricated with commercial BaMgAl10O17:Eu2+blue phosphors, (Ba,Sr)2(SiO4):Eu2+green phosphors, and the as-prepared Na2Gd2B2O7:0.35Eu3+red phosphors as well as a 395 nm LED chip. The device exhibited CIE coordinates of (0.4367, 0.3987), a high color rendering index (CRI = 92.2), a low correlated color temperature (CCT = 2960 K), and a luminous efficacy of 40.65 lm W-1. The observed results strongly indicate that the as-prepared Na2Gd2B2O7:Eu3+phosphors may be used as the red emitting component in pc-WLEDs.