A high-performance ceramic composite anode for protonic ceramic fuel cells based on lanthanum strontium vanadate

作者：Song Sang Hyun; Yoon Sung Eun; Choi Jaewon; Kim Byung Kook; Park Jong Sung^*

来源：International Journal of Hydrogen Energy, 2014, 39(29): 16534-16540.

DOI：10.1016/j.ijhydene.2014.03.219

• Solid oxide fuel cells
• Protonic ceramics
• Infiltration
• Composite electrodes
• Lanthanum strontium vanadate

The composite electrodes for protonic ceramic fuel cells (PCFC) were fabricated by infiltration of (La0.8Sr0.2)FeO3-delta (LSF) cathode and (La0.7Sr0.3)V0.90O3-delta (LSV) anode into a porous protonic ceramic, Ba(Ce0.51Zr0.30Y0.15Zn0.04)O3-delta (BCZY-Zn), respectively. Further, Pd-ceria catalysts were added into the composite anode. In the same method, the oxygen ion conducting fuel cells with the yttria-stabilized zirconia as an electrolyte (YSZ cell) were also fabricated. At 973 K, the non-ohmic area specific resistance (ASR) of PCFC (0.09 Omega cm(2)) was much smaller than that of the YSZ cell (0.28 Omega cm(2)) although the protonic conductivity of BCZY-Zn was slightly smaller than the oxygen ion conductivity of YSZ. According to the analysis of the symmetric cells with BCZY-Zn as an electrolyte, the LSV-composite anode showed better performance than the LSF-composite cathode at low temperatures.

• 出版日期2014-10-2