EROSIVE WEAR OF INCONEL 625 ALLOY COATINGS DEPOSITED BY CMT METHOD

作者：Solecka M^*; Kopyscianski M; Kusinski J; Kopia A; Radziszewska A

来源：Archives of Metallurgy and Materials, 2016, 61(2): 1201-1206.

DOI：10.1515/amm-2016-0199

• Inconel 625
• erosion wear
• solid particles erosion
• alloys

The article presents the investigation results concerning the determination of the characteristics of erosive wear caused by the impact of Al2O3 solid particles on the surface of Inconel 625 alloy after plastic working and the same material after weld cladding process using the CMT method. Erosion wear tests were performed at two temperatures: 20 degrees C and 650 degrees C. The erosion tests were conducted using the standard ASTM G76. A jet with a specified abrasive waight was directed to the surface of the tested material at an a impingement angle varied in the range of 30-90 degrees at a velocity imparted to the abrasive by the medium, which was compressed air. The eroded surface was examined using a scanning electron microscope (SEM), while the depths of craters caused by the erosion tests were measured with an optical profilometer. The predominant mechanisms of the formation of mass losses during solid particle erosion were microcutting and microfissuring.

• 出版日期2016-6