A 3D graphene interface (Si-doped) of Ag matrix with excellent electronic transmission and thermal conductivity via nano-assembly modification

作者：Ye, Xianzhu; Li, Ming; Zhang, Yafei^*

来源：Journal of Physics D: Applied Physics , 2018, 51(16): 165306.

DOI：10.1088/1361-6463/aab633

• nano-Ag
• graphene
• assembly
• electrical transmission
• thermal conductivity

The wide development of electronic materials requires higher load capacity and high temperature resistance. In this study, a novel architecture was fabricated consisting of a 3D reduced graphene oxide (rGO)-Si interface using a simple nano-assembly sintering to achieve high current capacity and excellent thermal features. Via the analysis of catalytic oxidation for methanol, the loading catalytic activity of nano-Ag still remained to a certain extent for the composite with 0.8 vol.% rGO. The final Ag-rGO composite apparently possesses a higher initial oxidation temperature and lower rate of oxidation for internal passing and shielding, and the thermal conductivity is significantly enhanced from 344 to 407 W m(-1) K-1. Importantly, with a 3D synergistic transportation network, the resistivity of the Ag-rGO composite is much lower than pure Ag, and with a longer conductive time under a stress condition of current density of 6.0 x 10(4) A cm(-2). Thermal-electronic features demonstrate that the dispersed graphene interface can efficiently suppress the primary failure pathways (high temperature) in Ag matrix and make it uniquely efficient for the advancement of microscale and thermal-management electronics.

• 出版日期2018-4-25
• 单位上海交通大学