Analysis of leakage current mechanisms in Pt/Au Schottky contact on Ga-polarity GaN by Frenkel-Poole emission and deep level studies

作者：Rao Peta Koteswara; Park Byungguon; Lee Sang Tae; Noh Young Kyun; Kim Moon Deock^*; Oh Jae Eung

来源：Journal of Applied Physics, 2011, 110(1): 013716.

DOI：10.1063/1.3607245

We report the Frenkel-Poole emission in Pt/Au Schottky contact on Ga-polarity GaN grown by molecular beam epitaxy using current-voltage-temperature (I-V-T) characteristics in the temperature ranging from 200 K to 375 K. Using thermionic emission model, the estimated Schottky barrier height is 0.49 eV at 200 K and 0.83 eV at 375 K, respectively, and it is observed that the barrier height increases with increase in temperature. The extracted emission barrier height (phi(t)) for Ga-polarity GaN Schottky diode by Frenkel-Poole theory is about 0.15 eV. Deep level transient spectroscopy study shows a deep level with activation energy of 0.44 eV, having capture cross-section 6.09 x 10(-14) cm(2), which is located between the metal and semiconductor interface, and trap nature is most probably associated with dislocations in Ga-polarity GaN. The analysis of I-V-T characteristics represents that the leakage current is due to effects of electrical field and temperature on the emission of electron from a trap state near the metal-semiconductor interface into continuum states associated with conductive dislocations in Ga-polarity GaN Schottky diode.

• 出版日期2011-7-1