Accelerated aging of unidirectional hybrid composites under the long-term elevated temperature and moisture concentration

作者：Boualem N; Sereir Z^*

来源：Theoretical and Applied Fracture Mechanics, 2011, 55(1): 68-75.

DOI：10.1016/j.tafmec.2011.01.007

• Accelerated aging
• Hybrid composites
• Temperature
• Moisture
• Strength ratio
• Hygrothermal stresses

Despite their high performances, composites with polymer matrix are very sensible to the increase in temperature and moisture concentration. During long years of services, both phenomena cause a critical transient hygrothermal transverse stresses, particularly at first-ply; i.e. at two edges of the composite plates. Therefore, significant degradation of hygrothermal characteristics and ultimate strengths of materials are occurred. To get an explicit relation between the durability and the damage probability of the composite, quadratic failure criterion in stress space is used. This criterion enables us to find a direct relation between transient hygrothermal stresses produced by the increase in temperature and moisture concentration and the ultimate strengths. It is necessary to calculate the strength ratio R from initial to saturation time for each condition imposed of temperature and moisture concentration. The strength ratio gives a point of view on the damage probability of the composite plates, where the rupture occurs if R = 1. In order to limit the consequences of simultaneous effects of temperature and moisture concentration, unidirectional hybrid composites in graphite epoxy was proposed. To reach this aim, hygrothermal transverse stresses are calculated through the thickness of unidirectional hybrid plate. Finally, the strength ratio was evaluated along of the plate with a gradual increase in temperature and moisture concentration.

• 出版日期2011-2