Adsorption of ammonia and water on functionalized edge-rich carbon nanofibers

作者：Takahashi Yusuke^*; Fujita Hirotaka; Sakoda Akiyoshi

来源：Adsorption, 2013, 19(1): 143-159.

DOI：10.1007/s10450-012-9435-x

• Carbon nanofiber
• Adsorption
• Ammonia
• Water

The preparation, characterization and ammonia and water adsorption properties of edge-rich carbon nanofibers (CNFs) were studied, including platelet CNFs (PCNFs) and cup-stacked CNFs (CSCNFs). Since PCNFs and CSCNFs have many chemically active exposed edges, functionalization by oxidizing the edges was carried out by ozone stream and by nitric acid. Transmission electron microscopy, N-2 adsorption isotherms and temperature-programmed desorption analysis showed that the nitric acid treatment partly destroyed the graphite structure of the PCNFs and created acid functional groups and micropores, whereas the ozone treatment created functional groups without damaging the structure. Ammonia adsorption isotherms clarified that NH3 adsorption on PCNFs and CSCNFs occurred mainly on oxygen-containing groups, whereas the adsorption on activated carbon fibers (ACFs) occurred on both oxygen-containing groups and the carbon surface without the functional groups, and the CSCNFs showed larger amounts of adsorbed ammonia compared to the PCNFs. Especially at a relatively low pressure range (< 0.2 atm), the PCNFs/CSCNFs/ACFs showed the same ammonia adsorption mechanism; that is, the one-to-one interaction between oxygen atoms in the functional groups and hydrogen atoms in ammonia molecules. In addition, the adsorption on the ACFs appeared to occur mainly by interaction with the carbon surface at relatively high pressure (0.3-1.0 atm). Our experimental results and previous findings suggest that NH3 adsorption on PCNFs is due mainly to NHaEuro broken vertical bar O hydrogen bonding between oxygen-containing groups and ammonia rather than to chemical bonding.

• 出版日期2013-2