A novel tubular oxygen-permeable membrane reactor for partial oxidation of CH4 in coke oven gas to syngas

作者：Zhang Yuwen^*; Su Kun; Zeng Fanlin; Ding Weizhong; Lu Xionggang

来源：International Journal of Hydrogen Energy, 2013, 38(21): 8783-8789.

DOI：10.1016/j.ijhydene.2013.05.019

• Tubular oxygen-permeable membrane reactor
• Catalytic partial oxidation
• Coke oven gas
• Syngas production

Dense BaCo0.7Fe0.2Nb0.1O3-delta (BCFNO) membrane tubes were prepared by slip casting and readily brazed to 310S stainless steel supports using a silver-based alloy. A novel tubular membrane reactor was constructed by placing a cylindrical Ni-based monolithic catalyst comdally around the tubular membrane and a conventional Ni-based catalyst-bed apart from the membrane tube. The novel membrane reactor was successfully applied to partial oxidation of CH4 in coke oven gas (COG). At 850 degrees C, 94% of CH4 conversion, 93% of H-2 and as high as 11.3 cm(3) cm(-2) min(-1) of oxygen permeation flux were obtained. The experimental H-2 and CO selectivity and CH4 conversion were close to the thermodynamically predicated ones. There was a good match in the coefficient of thermal expansion (CTE) among BCFNO membrane, Ag-based alloy and 310S metal support. Long-term operation test results indicate that the novel tubular BCFNO membrane reactor exhibited not only high activity but also good stability for the partial oxidation of CH4 in COG to syngas.

• 出版日期2013-7-17
• 单位上海大学